LAUSR

Due to very high strenght, low thermal conductivity, and high work hardening rate, the machinability of nickel-based superalloys is poor at room temperature. Laser-assisted machining (LAM) can provide a better aspect of machining such alloys. Since the wavelength of Nd:YAG laser is about 1/10th of that of CO2 laser, absorption and heating efficiency of Nd:YAG laser is much higher on metals and especially superalloys. Transmission of Nd:YAG laser through fiber optics to the heating point on the workpiece is a simple task during machining. This makes the LAM process more convenient and practical than the CM process. In this study a model is introduced for LAM of waspaloy, and its machinability is evaluated in terms of ease of material removal. Also, a temperature generation model is introduced for the Nd:YAG laser beam. Furthemore, wear behavior of an uncoated tungsten carbide and the formed chips were compared during the LAM and the CM of waspolay. To study the wear mechanism, the worn cutting tool was studied via scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS). The formed chips were also evaluated via SEM and optical microscopy. Based on the results, the optimum LAM conditions were obtained at a cutting speed of 24 m/min and a feed rate of 0.06 mm/rev when a 400 W laser mean power and 80 Hz frequency are applied. Under these conditions, the temperature ahead of the cutting tool edge on the surface of workpiece was estimated to be 524°C. In comparison with CM, a significant improvement in tool wear and a better chip morphology were achieved through LAM, and also specific cutting energy and surface roughness were reduced by 25 and 20%, respectively.