The two-dimensional (2D) insulating material hexagonal boron nitride (h BN) has attracted much attention as the active medium in memristive devices due to its favorable physical properties, among others, a… Click to show full abstract
The two-dimensional (2D) insulating material hexagonal boron nitride (h BN) has attracted much attention as the active medium in memristive devices due to its favorable physical properties, among others, a wide bandgap that enables a large switching window. Metal filament formation is frequently suggested for h-BN devices as the resistive switching (RS) mechanism, usually supported by highly specialized methods like conductive atomic force microscopy (C-AFM) or transmission electron microscopy (TEM). Here, we investigate the switching of multilayer hexagonal boron nitride (h-BN) threshold memristors with two nickel (Ni) electrodes through their current conduction mechanisms. Both the high and the low resistance states are analyzed through temperature-dependent current-voltage measurements. We propose the formation and retraction of nickel filaments along boron defects in the h-BN film as the resistive switching mechanism. We corroborate our electrical data with TEM analyses to establish temperature-dependent current-voltage measurements as a valuable tool for the analysis of resistive switching phenomena in memristors made of 2D materials. Our memristors exhibit a wide and tunable current operation range and low stand-by currents, in line with the state of the art in h-BN-based threshold switches, a low cycle-to-cycle variability of 5%, and a large On/Off ratio of 10${^7}$.
               
Click one of the above tabs to view related content.