LAUSR

Colloidal perovskite quantum dots represent one of the most promising materials for applications in solar cells and photoluminescences. These devices require a low density of crystal defects and a high yield of photogenerated carriers, which are difficult to realize in tin-halide perovskite because of the intrinsic instability of tin during nucleation. Here, an enhancement in the luminescent property of tin-halide perovskite nanoplates (TPNPs) that are composed of strongly coupled layered structures with the chemical formula of PEA2 SnX4 (PEA = C6 H5 (CH2 )2 NH3 , X = Br, I) is reported. TPNPs (X = I) show an emission at a wavelength of 640 nm, with high quantum yield of 6.40 ± 0.14% and full width at half maximum (FWHM) as small as 36 nm. The presence of aliphatic carboxylic acid is found to play a key role in reducing the tin perovskite defect density, which significantly improves the emission intensity and stability of TPNPs. Upon mixing iodo- and bromo- precursors, the emission wavelength is successfully tuned from 640 nm (PEA2 SnI4 ) to 550 nm (PEA2 SnBr4 ), with a corresponding emission quantum yield and FWHM of 0.16-6.40% and 36-80 nm, respectively. The results demonstrate a major advance for the emission yield and tunability of tin-halide perovskites.