Magnetite (Fe3O4) has a large theoretical reversible capacity and rich Earth abundance, making it a promising anode material for LIBs. However, it suffers from drastic volume changes during the lithiation process, which lead to poor cycle stability and low-rate performance. Hence, there is an urgent need for a solution to address the issue of volume expansion. Taking inspiration from how glycophyte cells mitigate excessive water uptake/loss through their cell wall to preserve the structural integrity of cells, we designed Fe3O4@PMMA multi-core capsules by microemulsion polymerization as a kind of anode materials, also proposed a new evaluation method for real-time repair effect of the battery capacity. The Fe3O4@PMMA anode shows a high reversible specific capacity (858.0 mAh g-1 at 0.1 C after 300 cycles) and an excellent cycle stability (450.99 mAh g-1 at 0.5 C after 450 cycles). Furthermore, the LiNi0.8Co0.1Mn0.1O2/Fe3O4@PMMA 200 mAh pouch cells exhibit a stable capacity (200.6 mAh) and high-capacity retention rate (95.5%) after 450 cycles at 0.5 C. Compared to the original battery, the capacity repair rate of this battery is as high as 93.4%. This kind of bionic capsules provide an innovative solution for improving the electrochemical performance of Fe3O4 anodes to promote their industrial applications.