LAUSR

This study evaluated the antierosive effect applying a modified acidulated phosphate fluoride (APF) gel containing nano‐hydroxyapatite (nHAp) on the enamel surface before erosion. After polishing, the exposed flat enamel surfaces (n = 7/group) from bovine incisors were treated with artificial saliva (S ‐ negative control), orange juice (ERO), APF gel (positive control) and APF_nHAp gel. All samples were subjected to six cycles of demineralization (orange juice, pH ~ 3.5, 10 min) followed by remineralization (saliva, 37°C, 1 hr). The enamel surface morphology, topography, and inorganic composition were analyzed using scanning electron microscopy, roughness testing, and micro energy‐dispersive X‐ray fluorescence spectrometry, respectively. The mean (standard deviation) roughness values (Ra, μm) were S, 0.13 (0.05); ERO, 0.25 (0.07); APF, 0.22 (0.08); and APF_nHAp, 0.17 (0.04). Ra values were significantly higher after ERO (p < .01) and APF (p < .05) treatments than after S. The enamel surface morphology was altered by the treatments, except for the S specimens. The mineral content of the enamel showed a clear trend with Ca and P reduction in the order of APF < S < APF_nHAp < ERO and APF < S < ERO < APF_nHAp, respectively. We can conclude that APF gel increased mineral concentration on the enamel. Moreover, the APF_nHAp material modified the composition and morphology of the enamel surface.