The rational structural design of the electrode materials is significant to enhance the electrochemical performance for potassium ion storage, benefiting from the shortened ion diffusion distance, increased conductivity, and pseudo-capacitance promotion. Herein, hydrated vanadium oxide (HVO) nanosheets with enriched oxygen defects are well confined into hollow mesoporous carbon spheres (HMCS), producing Od -VOH@C nanospheres through one-step hydrothermal reaction. Attributed to the restricted growth in the HMCS, the HVO nanosheets are loosely packed, generating abundant interfacial boundaries and large specific areas. As a result, Od -VOH@C nanospheres show increased reaction kinetics and well buffer the volume effects for the K+ storage. Od -VOH@C delivers stable capacities of 138 mAh g-1 at 2.0 A g-1 over 10 000 cycles in half-cells attributed to the high pseudo-capacitance contribution. The K+ storage mechanism of insertion and conversion reaction is confirmed by ex situ X-ray diffraction, Raman, and X-ray photoelectron spectroscopy analyses. Moreover, the symmetric potassium-ion capacitors of Od -VOH@C//Od -VOH@C deliver a high energy density of 139.6 Wh kg-1 at the power density of 948.3 W kg-1 .