LAUSR

Urea formaldehyde (UF) resin-impregnated Chinese fir (Cunninghamia lanceolata (Lamb.)Hook.) was dried at different temperatures in an atmospheric pressure superheated steam dryer. Drying characteristics, moisture content, drying rate, temperature profile, drying defects, and color change were investigated. The moisture content was reduced from 66.21 to 11.79% within 30 h without causing severe drying defects; in contrast, the conventional hot air process required 7–8 days. After 25 h of drying, the temperatures at both the center and the surface of wood remained stable. After 34.5 h, the surface temperature gradually approached the steam temperature. The color of the superheated steam dried Chinese fir appeared slightly more intense yellow and red than the control. Investigation of the UF-impregnated Chinese fir wood by scanning electron microscopy (SEM) revealed that the majority of the lumens and voids, including the microvoids in wood structure, was filled with urea formaldehyde resin.