Currently, there is an environmental pollution problem generated in part by packaging materials produced from non-biodegradable synthetic polymers made from petroleum. However, these can be replaced with biodegradable materials made from cassava starch (CS) and natural rubber (NR). In the work described, a novel biopolymer film was obtained from the CS and NR using glycerol (GE) as a plasticizer in a water-based system. The physical properties of an 95/5 CS/NR blend films with the addition of NR and with varying GE contents were studied based on their swelling ratio, moisture content, moisture absorption, mechanical properties and biodegradability in soil. The results showed that the moisture content and moisture absorption tended to be directly proportional to the GE content, while the moisture content and moisture absorption of the sample decreased as a function of the NR content. The swelling ratio of the 95/5 CS/NR blend slightly decreased as a function of the NR and GE content. Surprisingly, the best swelling ratio of 350% was found at 10% NR. The elongation at break of the CS/NR blend was improved by the addition of GE. The contact angle of the 95/5 CS/NR blend decreased as a function of the GE. With increased NR in the composite, an increasing, trend in the contact angle was found. Further, the 95/5 CS/NR blend exhibited good transparency when it was applied as a coating to delay the ripening of bananas, the results were positive. Moreover, the film showed decomposition well in natural soil.