LAUSR

A methodology is presented for the use of the oxide scale that develops in polycrystalline Ni-base superalloys at service temperature, as a speckle pattern for μm-scale resolution strain measurements. Quantitative assessment of the heterogeneous strain field at the grain scale is performed by high-resolution SEM digital image correlation under monotonic and cyclic loading in polycrystalline Ni-base superalloys up to 650 ∘C. In the René 88DT superalloy, strain localization is observed near twin boundaries during low cycle fatigue (LCF) at intermediate temperatures, correlating with activation of {111} 〈110〉 and {111} 〈112〉 slip systems. A strong correlation between the microstructural configuration that promotes strain localization during monotonic loading and crack initiation at 650 ∘C in low cycle fatigue was observed.