LAUSR

The manuscript presents the effect of laser surface melting (LSM) on the microstructural variations and pitting corrosion resistance of 304L SS weldment fabricated by gas tungsten arc welding of 304L SS plates using 308L SS filler wire. The weld region was examined by X-ray radiography for defect detection. LSM of 304L SS weldment was performed using Nd:YAG pulsed laser. Microstructural evaluation was carried out using optical and electron back scatter diffraction techniques. The microstructure of 304L SS base was found to be austenitic, while the weld region of 304L SS weldment contained delta ferrite distributed in austenite matrix. The microstructure of LSM 304L SS weldment was found to be homogeneous austenite matrix with sparsely distributed ferrite. Ferrite measurements showed a decrease in the percentage ferrite in the fusion zone of 304L SS weldment after LSM. A profound enhancement in the pitting corrosion resistance was observed after LSM, which could be attributed to the homogeneous microstructure and decrease in the ferrite content. Pit density was found to be higher in the heat-affected zone of the weldment. Very few pits were observed in the LSM 304L SS weldment compared to the as-weldment.