Nanostructuring is known to be an effective method to improve thermoelectric performance but, generally, it requires complex procedures and much labor. In the present study, self-assembled nanometer-sized composite structures of… Click to show full abstract
Nanostructuring is known to be an effective method to improve thermoelectric performance but, generally, it requires complex procedures and much labor. In the present study, self-assembled nanometer-sized composite structures of silicon (Si) and chromium disilicide (CrSi2) were easily fabricated by the rapid solidification of a melt with a eutectic composition. Ribbon-like samples were obtained with a dominant nanostructure of fine aligned lamellae with a spacing range of 20–35 nm. The thermoelectric power factor of the ribbon was observed to be 1.2 mW/mK2 at room temperature and reached 3.0 mW/mK2 at 773 K. The thermal conductivity was 65% lower than that of a bulk eutectic sample. The results suggest that this method is promising for fabricating an effective nanostructure for thermoelectric performance.
               
Click one of the above tabs to view related content.