This paper introduces a facile and effective route to decorate micro-sized silver particle surfaces with Ag/AgI nanoclusters through a wet chemical reaction at room temperature using iodine and ethanol as reactant and solvent, respectively. Photosensitivity of AgI is utilized in the route, and AgI decomposes into Ag upon contact with sunshine, forming Ag/AgI nanoclusters. The modified micro-sized Ag particles showed sinterability even at 200°C and formed rigid electrical conductive networks at 350°C. Moreover, sintered film containing the modified Ag particles reached the best conductivity, 9.35 mΩ/sq, after sintering at 350°C for 20 min, while the film with untreated control Ag particles obtained its best conductivity at 400°C. The excellent sinterability should be attributed to the nanoclusters which served as a sintering aid during the heating process. However, increase of sintering temperature and time destroyed densification and conductivity of the sintered film containing the modified particles.