The present study attempts to examine monotonic and fatigue response of friction-stir-welded (FSW) Al 6061-T6 joints. Surface-rolling techniques of in situ and sequential were adapted to evaluate the influence of generated surface deformation on static and fatigue properties of the welded joints. A custom-made tool with four balls with the capability of changing in ball sizes and ball indentations was employed to burnish, while stir-weld beads are formed in situ. The sequential technique, however, rolled the top surface of joints after completion of welding operation. Tensile strength values measured from in situ-rolled FSW joints undergoing static loading were found to be, respectively, 25 and 40% higher with ball sizes of 6 and 8 mm as compared with those un-burnished FSW joints. Fatigue lives of in situ-rolled samples were also enhanced, respectively, 4 and 6 times in magnitudes for these ball diameters. Sequential rolling technique, however, resulted in a negligible elevation in static and fatigue properties of FSW joints. The in situ rolling process on the FSW samples led to more uniform and refined grains especially in HAZ region as compared with those of AW specimens. This resulted in higher static strength and longer fatigue lives. SEM images of the fractured surface revealed brittle fracture over crack initiation site followed by a mixed cleavage and ductile dimples at the rupture stage.