NiCr/Ag-Mo composite coating was fabricated by atmospheric plasma spray technology using clad powders as the feedstock. Its tribological properties at variable temperature were evaluated using a ball-on-disk high-temperature tribometer in… Click to show full abstract
NiCr/Ag-Mo composite coating was fabricated by atmospheric plasma spray technology using clad powders as the feedstock. Its tribological properties at variable temperature were evaluated using a ball-on-disk high-temperature tribometer in air. The results showed that compared with NiCr, the NiCr/Ag-Mo composite coating exhibited better lubrication effect and higher wear resistance at all test temperatures, especially above 600 °C. At 800 °C, NiCr/Ag-Mo composite coating showed the lowest friction coefficient of about 0.2 and its corresponding wear rate reached 2.5 × 10−5 mm3/Nm. Characterizations of NiCr/Ag-Mo composite coating revealed that at temperatures below 400 °C, Ag was smeared and spread onto the wear surface, reducing the friction and wear. At temperature above 500 °C, the Ag2MoO4 lubrication film formed by tribo-oxidation significantly improved the coating’s lubrication effect and wear resistance.
               
Click one of the above tabs to view related content.