The 600 and 800 °C isothermal sections of the Al-Sb-Cr ternary system were studied by scanning electron microscopy, energy dispersive x-ray spectroscopy, and x-ray diffraction. No ternary compound was found in this system at either 600 or 800 °C. AlSb can equilibrate with all phases in both the 600 and 800 °C isothermal sections except Cr. Ten three-phase regions were clearly identified in the Al-Sb-Cr ternary system at 600 °C and seven three-phase regions were confirmed in the 800 °C isothermal section.
               