Thermodynamic analysis of oxygen-enriched direct smelting of jamesonite concentrate is reported in this article. First, the occurrence state of lead, antimony and other metallic elements in the smelting process was investigated theoretically. Then, the verification test was carried out. The results indicate that lead and antimony mainly exist in the alloy in the form of metallic lead and metallic antimony. Simultaneously, lead and antimony were also oxidized into the slag in the form of lead-antimony oxide. Iron and copper could be oxidized into the slag in the form of oxides in addition to combining with antimony in the alloy, while zinc was mainly oxidized into the slag in the form of zinc oxide. The verification test indicates that the main phases in the alloy contain metallic lead, metallic antimony and a small amount of Cu2Sb, FeSb2 intermetallic compounds, and the slag is mainly composed of kirschsteinite, fayalite and zinc oxide, in agreement with the thermodynamic analysis.