The relationship between the viscoelasticity and bending recovery responses of PI and PEEK films were studied as well as the effect of physical aging treatment on these properties. The residual… Click to show full abstract

The relationship between the viscoelasticity and bending recovery responses of PI and PEEK films were studied as well as the effect of physical aging treatment on these properties. The residual elastic modulus (Er) and degree of aging of the films were measured from the stress relaxation-recovery experiment using DMA and the enthalpy relaxation endotherms near glass transition temperature using DSC, respectively. The instantaneous bending recovery ratio (BR+) of the films was measured from the change in radius of curvature before and after the bending under the condition of 85 °C/85%RH/24 hr. The DMA test was also performed at 85 °C in order to evaluate the progression of the stress relaxation during bending. The Er and BR+ values showed good correlation, and higher contributions of elastic response or longer delay of the stress relaxation led to improved bending recovery. Films with BR+ values close to zero can be obtained if the conditions of Er <0.05 are satisfied. A physical aging method was proven to be effective for controlling the viscoelastic response of the films; it contributes to the retardation of stress relaxation. The optimum physical aging temperatures were 200 °C for PI and 130 °C for PEEK, respectively. Both films achieved a sufficient aging effect with the treatment time of 24 hours.

Keywords: recovery; peek films; relaxation; effect; bending recovery; physical aging

Journal Title: Fibers and Polymers
Year Published: 2019

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.