Electrophoretic painting (E-paint) was prepared on AZ31 Mg alloy samples pretreated in cerium conversion coating (CeCC) solutions with various ratios of ethanol and water mixture and its characteristics, adhesion and corrosion resistance were investigated. It was found that CeCC formed on AZ31 Mg alloy in a CeCC solution without ethanol was partly cracked structure and mainly consisted of Mg(OH)2/MgO, which exhibited weak adhesion with E-painting layer after water immersion test, and low corrosion resistance, as indicated by rapid formation of blisters and paint delamination during salt spray test. The addition of ethanol promoted the growth of a fine nano-crystalline CeO2 layer over the entire substrate surface. The E-paint on AZ31 pretreated in the CeCC solutions with addition of ethanol showed also improved corrosion resistance, as represented by the delayed time for paint delamination and blister formation. The E-paint layers on the CeCC layers formed in solutions containing 50–80 vol% ethanol showed stronger adhesion and better corrosion resistance than those formed on the samples treated in a non-ethanol containing CeCC solution.