Austempered ductile iron (ADI) is known to have a good combination of mechanical properties due its unique ausferrite microstructure. The strength of ADI is mainly a function of the austempering temperature and the stability of ausferrite matrix. To increase the stability of the ausferritic matrix, two stage austempering processes was developed. During this investigation, in the Ist step, ductile iron specimens were austenitized at 900 °C for 60 min followed by quenching to 250 °C in salt bath. In the IInd step, after quenching at 250 °C, the salt bath was gradually heated to 350 °C, 400 °C and 450 °C respectively where specimen were soaked for 120 min. The tensile strength and impact strength were evaluated according to ASTM standards. The results were compared with that obtained by conventional austempering process by quenching directly into salt bath at 400 °C for 120 min. Both tensile and impact strength were found to have improved by two step austempering process. During Ist stage of austempering, martensite was observed while during IInd stage of austempering microstructures revealed acicular ferrite and carbon stabilized austenite. The fractographic examination revealed mixed type of fracture mode and intergranular fracture was seen under SEM. It was further observed that the tensile strength decreased whereas the impact strength increased with IInd stage of austempering temperature.