LAUSR

A surface engineering strategy was proposed to design hierarchically porous structure on fibrous carbon cathodes with O/N heteroatom functional groups. High-energy and anti-self-discharge Zn-ion hybrid supercapacitors (ZHSs) were realized. ZHS electrochemistry was investigated and new insights were provided. Aqueous Zn-ion hybrid supercapacitors (ZHSs) are increasingly being studied as a novel electrochemical energy storage system with prominent electrochemical performance, high safety and low cost. Herein, high-energy and anti-self-discharge ZHSs are realized based on the fibrous carbon cathodes with hierarchically porous surface and O/N heteroatom functional groups. Hierarchically porous surface of the fabricated free-standing fibrous carbon cathodes not only provides abundant active sites for divalent ion storage, but also optimizes ion transport kinetics. Consequently, the cathodes show a high gravimetric capacity of 156 mAh g −1 , superior rate capability (79 mAh g −1 with a very short charge/discharge time of 14 s) and exceptional cycling stability. Meanwhile, hierarchical pore structure and suitable surface functional groups of the cathodes endow ZHSs with a high energy density of 127 Wh kg −1 , a high power density of 15.3 kW kg −1 and good anti-self-discharge performance. Mechanism investigation reveals that ZHS electrochemistry involves cation adsorption/desorption and Zn 4 SO 4 (OH) 6 ·5H 2 O formation/dissolution at low voltage and anion adsorption/desorption at high voltage on carbon cathodes. The roles of these reactions in energy storage of ZHSs are elucidated. This work not only paves a way for high-performance cathode materials of ZHSs, but also provides a deeper understanding of ZHS electrochemistry.