Abstract The ability of delivering chemical information from peak shift phenomena has ever since made X-ray photoelectron spectroscopy (XPS) an ideal tool for material characterization in Li-ion batteries (LIB). Upon investigation, charging is inevitable as most of the chemical species involved are non-conducting. Thus, the binding energy (BE) scale must be corrected to allow an accurate interpretation of the results. This is usually done using the peak position of the ubiquitous surface carbon contamination detectable for all Li-ion battery relevant materials. We herein report on the occurrence of peak shift phenomena that can be observed when investigating surface layers on graphite anodes using sputter depth-profiling. These shifts, however, are not related to classical static electric charging, but are depending on the state of charge (lithiation) of the anode material. The observations presented are in agreement with previous findings on other Li-containing materials and are obviously caused by the presence of Li in its elemental state. As aging and failure mechanisms in LIBs are closely linked to electrolyte reaction products on electrode surfaces it is of high importance to draw the correct conclusions on their chemical origin from XP spectra. In order to avoid misinterpretation of the BE positions, implanted Ar can be used for identification of relevant peak positions and species involved in the phenomena observed.