Abstract In this study, Mg-containing hydroxyapatite coatings on Ti-6A1-4 V alloy for dental materials were researched using various experimental instruments. Plasma electrolytic oxidation (PEO) was performed in electrolytes containing Mg (symbols of specimens: CaP, 5M%, 10M%, and 20M%) at 280 V for 3 min. The electrolyte used for PEO was produced by mixing Ca(CH 3 COO) 2 ·H 2 O, C 3 H 7 NaCaO 6 P, and MgCl 2 ·6H 2 O. The phases and composition of the oxide films were evaluated by X-ray diffraction and field-emission scanning electron microscopy with energy dispersive X-ray spectrometry. The irregularity of the surface, pore size, and number of pores decreased as the Mg concentration increased. The ratio of the areas occupied and not occupied by pores decreased as the Mg concentration increased, with the numbers of both large and small pores decreasing with increasing Mg concentration. The number of particles on the internal surfaces of pores was increased as the Mg content increased. Mg content of all samples containing Mg ions showed higher in the pore outside than that of pore inside, whereas the Ca content was higher inside the pores. The P content of samples with the addition of Mg ions showed higher values inside the pores than outside. The Ca/P and [Mg + Ca]/P molar ratios in the PEO films decreased with Mg content. The crystallite size of anatase was increased with increasing Mg concentration in the solution.