Abstract The chemical compositions, phases and structures of two oxide films on Alloy 690TT following exposure for 4400 h in pure water with and without lead at 320 °C were studied by surface analysis techniques. The analysis of a lead-doped oxide film prepared by a focused ion beam (FIB) demonstrated that both Cr-rich and Ni-rich oxides were alternatively distributed within the outer layer, whereas the inner layer was porous and poorly protected, causing severe corrosion of the alloy and a thicker film was formed. A duplex film model was proposed for the effects discussion of lead on the oxidation mechanism.
               