LAUSR

Abstract A sturdy self-cleaning and anticorrosion superhydrophobic coating based on poly(phenylene sulfide) (PPS) matrix has been successfully fabricated by combination of sol-gel and spraying technology without using any fluorine materials. The prepared coating possessed excellent superhydrophobicity with the water contact angle (WCA) (161 ± 1.2)° and slide angle (SA) (2 ± 1.5)°, which was ascribed to the synergistic effect of low-surface energy material amino silicon oil (ASO) and the binary potassium titanate whisker-silica (PTW-SiO2) composite particles formed by in-situ growth of SiO2 on modified PTW via sol-gel. Moreover, The PPS/ASO/PTW-SiO2 superhydrophobic coating exhibited decent self-cleaning property with clean surface even after 100 times immersion in muddy solution. The abrasion test demonstrated that the mechanical stability of prepared coating was about 2 times of the pure PPS coating. Simultaneously, the potentiodynamic polarization and electrochemical impedance spectroscopy testified the excellent corrosion resistance of prepared coating with the performance of lower corrosion current (1.289 × 10−10 A/cm2) and high protection efficiency (99.999%) even after immersion in 3.5 wt.% NaCl solution for 28 days. It is believed that this sturdy self-cleaning and anti-corrosion superhydrophobic coating might have a promising application prospect in industry.