Abstract Lithium-rich layered materials have received much attention because of their high specific capacity and high energy density. Unfortunately, they suffer from irreversible capacity loss, low initial Coulombic efficiency and poor cyclability. Here we report a facile co-precipitation method to synthesize uniform single-crystal Li-rich Li[Li0.2Mn0.54Ni0.13Co0.13]O2 nanoplates without using any template. Subsequently, a Co3O4 shell is in situ grown on the Li-rich nanoplates through a hydrothermal method, leading to spinel/layered heterostructures. The electrode made of conformal heterostructured Li-rich/Co3O4 nanoplates delivers a high discharge capacity of 296 mA h g−1 at 0.1 C with an initial Coulombic efficiency of 84%. The capacity retention reaches 83.2% with a discharge capacity of 223 mA h g−1 after 160 cycles at 0.2 C during the potential window ranging from 2.0 to 4.8 V. The enhanced electrochemical performance of the resulting Li-rich/Co3O4 nanoplates benefits from the unique conformal heterostructure as well as the electrochemically active LixCoOy generated between the reaction of Co3O4 shells and the extracted Li2O during charging/discharging processes.