Abstract In order to improve the performance of proton exchange membrane fuel cell (PEMFC), the optimization of electrostatic spraying of membrane electrode was conducted. The influence of the spraying voltage on morphology, elemental composition of catalyst layer, and performance of the PEMFC were investigated. The results show that increasing spraying voltage could reduce agglomeration of the carbon-supported platinum particles, leading to more uniform pore distribution. High voltage did not accelerate oxidation of platinum catalyst. A high electrochemical active surface area of 26.18 m2/gpt was obtained when the platinum-carbon catalyst layer was deposited in cone jet mode. With further increasing spraying voltage, the total ohmic resistance and catalytic activity were changed slightly, whereas the charge transfer resistance was increased. Using the optimized electrostatic spraying parameters (injection rate = 100 μL min−1, spraying voltage = 8.5 kV, and working distance = 12 mm), a peak power density of 1.408 W cm−2 was obtained with an output voltage of 0.451 V.