LAUSR

ABSTRACT Lithium-sulfur (Li-S) batteries have received extensive attention due to their high theoretical specific energy density. However, the utilization of sulfur is seriously reduced by the shuttle effect of lithium polysulfides and the low conductivity of sulfur and lithium sulfide (Li2S). Herein, we introduced bimetal-organic frameworks (Co/Zn-ZIF) derived cobalt and nitrogen-doped carbons (Co/N-C) into Li-S batteries through host design and separator modification. The Co/N-C in Li-S batteries effectively limits the shuttle effect through simultaneously serving as polysulfide traps and chemical catalyst. As a result, the Li-S batteries deliver a high reversible capacity of 1614.5 mAh/g and superior long-term cycling stability with a negligible capacity decay of only 0.04% per cycle after 1000 cycles. Furthermore, they have a high area capacity of 5.5 mAh/cm2.