Geometrical morphology optimisation of laser drilling in B4C ceramic: From plate to hollow microsphere

Photo from archive.org

Abstract Boron carbide (B 4 C) ceramic plates with 400-µm thickness and hollow microspheres were used for hole machining study with a fibre laser. The diameter, hole circularity, taper angle,… Click to show full abstract

Abstract Boron carbide (B 4 C) ceramic plates with 400-µm thickness and hollow microspheres were used for hole machining study with a fibre laser. The diameter, hole circularity, taper angle, and recast layer were evaluated as functions of processing parameters such as the peak power and the ablation time. Scanning electron microscope (SEM) was used to observe surface morphologies of drilled materials and the attached energy-dispersive spectrometer was used for elemental analyses of recast layers around holes. Based on the results of characterisations, holes on front side were found to have a larger diameter but a worse circularity than those on back side under different conditions. The taper angle was steady near 1.8° with the increase in laser parameter values. To obtain holes on B 4 C ceramic with relatively good quality, the peak power and the ablation time should be controlled to be about 40 W and in 5–10 ms. In addition, compared with previous reports, superior holes drilled on B 4 C hollow microspheres with a better circularity and smooth layer on the inner wall can be obtained.

Keywords: geometrical morphology; laser drilling; morphology optimisation; optimisation laser; hollow; drilling b4c

Journal Title: Ceramics International
Year Published: 2018

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.