LAUSR

Abstract In service tensile and compressive stresses occur in refractory linings, these stresses lead to creep of refractories. Ordinary refractories experience creep of the primary stage and may further proceed to the secondary and tertiary creep stage. For the development of advanced material models for finite element simulations it is necessary to investigate the creep behavior in all three creep stages under tensile and compressive loads. Hence, two advanced high temperature uniaxial creep testing devices, applying a wide range of tensile and compressive loads, were used to determine the three creep stages in a reasonable time under service related loading conditions. The Norton–Bailey creep equations and an inverse identification procedure were applied for the evaluation of the experimental results. A magnesia refractory was studied at elevated temperatures and its respective creep parameters for each stage were determined. The stress dependency on the creep behavior can be seen clearly on the creep curves and the corresponding creep parameters. Furthermore, a comparative study of creep parameters and creep rates was performed between the magnesia refractory and a magnesia-chromite refractory. The results demonstrate the significant asymmetrical creep behavior in tension and compression for both materials. The creep investigation in this paper favors the requirement for consideration of the three stage creep behavior and the asymmetrical creep behavior in thermomechanical modelling activities of industrial vessels.