Abstract Spherical α-Al 2 O 3 powders were synthesized from a mixed solution consisting of Al 2 (SO 4 ) 3 ·18H 2 O, Al(NO 3 ) 3 ·9H 2 O and CH 4 N 2 O by hydrothermal method with muffle calcination and microwave calcination. Effects of raw material ratio, reaction temperature, and filling factor on properties of products were investigated. Properties of thermal behavior, functional groups, phase composition, microstructure and specific surface of precursors and products were characterized by DSC-TG, FT-IR, XRD, SEM and BET, respectively. Results show that SO 4 2− plays an important role in the sphere formation of precursors and particle size can be changed by adding different proportion of NO 3 − . Precursors are amorphous spherical hydrated alumina containing SO 4 2− , and the conversion of crystalline phase is from amorphous to γ-phase and then to α-phase at 1100 °C. Spherical morphology can be retained after crystallization to α-Al 2 O 3 . Compared with muffle furnace, Microwave calcination can increase calcining rate by three times and reduce insulation time by three quarters. When hydrothermal reaction temperature is 120 °C, the particles can be precipitated with good sphericity and narrow grain size distribution. If hydrothermal reaction temperature is too high or too low, spherical morphology can't be obtained. Size of the particles can be regulated by the different raw material ratio and filling factor from 800 nm to 3 μm, and specific surface area is in the range of 8 m 2 /g∼15 m 2 /g.