Abstract In this study, (1-x) Bi0.5(Na0.78K0.22)0.5TiO3-xBaTiO3 lead-free piezoelectric ceramics were prepared by sol-gel method. The effects of K+ doping modification and BaTiO3 solution modification on the microstructure and electrical properties… Click to show full abstract
Abstract In this study, (1-x) Bi0.5(Na0.78K0.22)0.5TiO3-xBaTiO3 lead-free piezoelectric ceramics were prepared by sol-gel method. The effects of K+ doping modification and BaTiO3 solution modification on the microstructure and electrical properties of bismuth sodium titanate based ceramics were investigated. The modified samples show pure perovskite structure without impurities. The coexistence of rhombohedral phase and tetragonal phase was observed in the samples (x = 0.06–0.12), which was verified by lattice parameters and Raman spectrum analysis. The introduction of BaTiO3 reduced the grain size and increased the density of the sample. The maximum electrical parameters (emax = 1887, d33max = 167 pC/N and kpmax = 45%) of the sample (x = 0.06) are significantly higher than those of other references, and the temperature stability of piezoelectric constant was greatly improved. The related mechanism was analyzed in detail by lattice theory and domain theory.
               
Click one of the above tabs to view related content.