Abstract Micron-sized lanthanum oxide powders are prepared by the calcination of lanthanum carbonate hydrate in microwave field. The decomposition process of lanthanum carbonate hydrate was analyzed by TG-DSC and indicates the reaction undergoes three stages, resulting in the generation of lanthanum oxide at 770 °C. For microwave assisted calcination, XRD patterns demonstrate that hexagonal La2O3 structure is initially formed after calcination at 650 °C for 2 h, and FT-IR analyses confirm the decomposition of precursor is complete after calcination at 750 °C for 2 h. SEM investigations reveal that 800 °C is the optimal calcination temperature to generate La2O3 powders with uniform morphologies. In comparison, conventionally calcination experiments are carried out in electrical furnace. Both XRD and FT-IR analyses are in consistence with TG-DSC, which indicate the temperature required for fully decomposition of lanthanum carbonate hydrate by conventional heating is higher than that of microwave heating. SEM images present irregular morphologies and wide particle size distribution of conventionally prepared samples. All the techniques are utilized to prove the feasibility of decomposing La2(CO3)3 to generate La2O3 in microwave field and highlight the advantages of microwave heating.