Abstract An overview of research on the synthesis of manganese titanates is presented. The xerogel of Mn–Ti–O–C–H composition was synthesized from manganese acetate and titanium tetrabutylate via liquid-phase method using organic solvents. The calcination of xerogel in air at 450 °C and 700 °C yielded manganese titanate precursors in the form of a nanostructured mixture of Mn2O3 and TiO2. Annealing at 1000 °C, manganese metatitanate MnTiO3 was obtained. Reference experiments with initial reagents included, separately, thermal decomposition of Mn(CH3COO)2×4H2O and the product of Ti(OC4H9)4 hydrolysis. The composition, structure, and properties of the products were studied using X-ray diffraction, scanning electron microscopy, elemental analysis, diffuse reflectance IR Fourier spectroscopy, thermogravimetry, and by measuring specific surface area. The data presented by these different techniques are basically consistent with each other (with an increase in the annealing temperature, an increase in globule size and decrease in specific surface area are observed; structuring occurs within the long- and short-range order; the size of the crystallites does not exceed that of the globules; elemental composition correlates with phase composition; the endothermic character of the reaction of MnTiO3 formation at 900 °C is confirmed by a thermodynamic calculation). Nevertheless, some unexpected effects were revealed (based on the FTIR diffuse reflection spectra, mixed oxide Mn–Ti–O is formed in the surface layer of particles already at 450 °C and 700 °C; etc.). Application of the proposed technique for modifying Al2O3 powders, with the aim of implementing low-temperature sintering of corundum ceramics, is discussed.