B4C particulate-reinforced Al-8.5 wt% Si-3.5 wt% Cu matrix composites: Powder metallurgical fabrication, age hardening, and characterization

Photo by neonbrand from unsplash

Abstract The present work investigates microstructural and mechanical properties of B4C particulate-reinforced Al-8.5 wt % Si-3.5 wt % Cu matrix composites prepared by a successive process of mechanical alloying (MA),… Click to show full abstract

Abstract The present work investigates microstructural and mechanical properties of B4C particulate-reinforced Al-8.5 wt % Si-3.5 wt % Cu matrix composites prepared by a successive process of mechanical alloying (MA), cold pressing, and pressureless sintering. The effects of B4C amount, milling duration, and heat treatment were investigated. The MA (for 0, 3, 5, and 7 h) in a high-energy vibratory ball mill was applied to elemental powder blends, in which 0, 5, 7.5, and 10 wt % B4C was incorporated as reinforcing particles. Mechanically alloyed (MAed) powders were uniaxially pressed and sintered for 2 h at 550 °C then subjected to an aging heat treatment to improve the mechanical properties. Based on XRD, SEM, and TEM microstructural investigations, compared to the as-blended case, the MAed powders possessed a semi-equiaxed morphology and homogenous structure, with higher lattice strain and smaller crystallite size. In addition, the Al-8.5 wt % Si-3.5Cu-xB4C (x = 0, 5, 7.5, and 10 wt %) composites consolidated from the MAed powders exhibited improved mechanical properties, including microhardness, wear resistance, and compressive strength. The hardness of the 5 h-MAed Al-8.5 wt % Si-3.5 wt % Cu-10B4C composite was 167 HV, and yield and compressive strength were 362 MPa and 454 MPa, respectively. This sample also exhibited one of the lowest wear rates, 5.82x10-5 mm3/m.N, roughly 17 and 10 times lower than that of the 5 h-MAed Al-8.5 wt % Si-3.5 wt % Cu sample and its as-blended counterpart, respectively. Furthermore, the hardness and compressive strength of 5 h-MAed Al-8.5 wt % Si-3.5 wt % Cu-10B4C composite increased to 231 HV and 475 MPa, respectively, after the age-hardening treatment.

Keywords: particulate reinforced; b4c particulate; matrix composites; age hardening; reinforced matrix

Journal Title: Ceramics International
Year Published: 2020

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.