Abstract Ni2+ modified MgTa2O6 ceramics with a trirutile phase and space group P42/mnm were obtained. The correlations between crystallographic characteristics and microwave dielectric performance of MgTa2O6 ceramics were systematically studied… Click to show full abstract
Abstract Ni2+ modified MgTa2O6 ceramics with a trirutile phase and space group P42/mnm were obtained. The correlations between crystallographic characteristics and microwave dielectric performance of MgTa2O6 ceramics were systematically studied based on the chemistry bond theory (PVL theory) for the first time. The results indicate that the introduction of Ni2+ causes a change in polarizability and the Mg-O bond ionicity, which contributes to the variation of dielectric constant. Moreover, the lattice energy, and packing fraction, full width at half maximum of the Raman peak of Ta-O bond, as the quantitative characterization of crystallographic parameters, regulate the dielectric loss of MgTa2O6 ceramics in GHz frequency band. In addition, the study of sintering behavior shows that the densification and micromorphology are the crucial factors affecting the microwave dielectric performance. Typically, Ni2+ doping on the A-site of MgTa2O6 can effectively promote the Q×f values to 173,000 GHz (at 7.43 GHz), which ensures its applicability in 5G communication technology.
               
Click one of the above tabs to view related content.