Abstract This is the first representation of novel sodalite zeolitic imidazolate framework-7 (ZIF-7) which has been made in ethanolic solution at room temperature via an ammonia atmosphere. High thermal stability up to 400 °C is representative of great persistence which has been proved by XRD and TG data. Chemical durability of the as-made ZIF-7 especially at boiled DMF exhibited by XRD patterns can present it as an interesting material without structural alteration after treatment in such harsh condition. Reversible phase transformation of ZIF-7 was totally checked by immersing in ethanol and DMF indicated that the framework can maintain its structural flexibility under heat and solvent treatment. Moreover, the “gate-opening” phenomenon performed by CO2 adsorption–desorption reveals structural breathing effect of ZIF-7 framework that makes it as potential material in CO2 adsorption/separation. In the end, the sacrificial metal-doped (Mn2+, Ni2+, Cu2+, Cd2+ and Ag+) ZIF-7 precursors were applied for preparation of their corresponded metal-doped ZnO as the heterogeneous catalyst to degrade Rhodamine-B (RhB) dye in water under UV-irradiation (up to 99% within 90 min by 0.5% Ag-ZnO (S15)). The recyclability experiment after 5 runs for the optimized catalyst demonstrated that the metal-doped ZnO can be operated consecutively without remarkable decreasing in its activity. These observations exhibit the excellent and beneficial properties of metal-doped ZnO can be as heterogeneous photocatalyst for the removal of organic contaminants in water.