Abstract A biobased and biocompatible thermoplastic elastomer (TPE) with superior 3D printability was demonstrated with great potential for customized manufacturing technologies and fabrication of biointegrated devices. The inherent structural and stereochemical disadvantages of biobased monomers, such as 2,5-furandicarboxylic acid, in comparison with today used petroleum based monomers like terephthalic acid generally lead to lower mechanical performance for the biobased replacement polymers. This is additionally enhanced by poor interfacial adhesion and fusion commonly encountered during customized manufacturing technologies like 3D printing. Herein, we demonstrate that in-situ polymerization in the presence of trace amounts of cellulose nanocrystals (CNCs) can homogeneously distribute the nanofiller leading to dramatically strengthened thermally 3D-printable bio-furan-based TPE. This TPE exhibited a tensile strength of 67 MPa which is 1.5–7-fold higher than the values reported for silicone and thermoplastic urethane, which are widely used in biomedical applications. In addition, the TPE had an impressive extensibility of 860% and negligible in vivo cytotoxicity; such properties have not been reported to date for bio-based or petrochemical TPEs. While a petrochemical 3D printed TPE counterpart retained only half of the tensile strength compared to the hot-pressed analogue, the 3D-printed biobased TPE in-situ modified with nanocellulose maintained 70–80% of its strength under the same experimental conditions. This is explained by inter-diffusion between interfaces facilitated by the nanocellulose and the furan rings. Using the ergonomic shape of a wrist as a 3D-printable design, we successfully manufactured a wearable thermal therapeutic device from the nanocellulose modified biobased TPE, giving promise for wide variety of future applications.