Abstract This paper investigates the autogenous sealing capability of curaua Textile Reinforced Concrete (TRC). Curaua is a high-performance natural fiber with excellent tensile strength and water absorption capacity. The curaua… Click to show full abstract
Abstract This paper investigates the autogenous sealing capability of curaua Textile Reinforced Concrete (TRC). Curaua is a high-performance natural fiber with excellent tensile strength and water absorption capacity. The curaua TRC mechanical behavior was evaluated through direct tensile and four-point bending tests. The autogenous mechanical recovery was analyzed by means of repeated bending and short-time creep tests. The specimens were submitted to three different environmental conditions (RH of 55%, cycles of sprayed water and 12-h water immersion) and their influence on crack sealing was evaluated. The TRC presented strain and deflection hardening behavior with a mean crack width of 50 µm. The combination of the hydrophilic nature of curaua fibers, the matrix with high pozzolanic content and narrow cracks, contributed to the autogenous sealing of the cracks and mechanical recovery of the specimens. Even under repeated and short-time creep tests, the curaua TRC did not lose its strength or strain capacities; and the mean crack width remained close to the ones submitted to the monotonic test. When submitted to sprayed water, all cracks were partially sealed after only four cycles.
               
Click one of the above tabs to view related content.