Abstract This paper presents the results of a comprehensive experimental work investigating the effect of glass fiber (GF) and polypropylene fiber (PPF) on the mechanical and microstructural properties of concrete as a function of the water/binder ratio and fiber content. Different water/binder ratios (0.30 and 0.35), GF and PPF contents (0.45, 0.90, and 1.35% by volume fractions), and curing times (7 and 28 d) were used during the experiment to prepare the concrete specimens. The compressive, four-point flexural, and splitting tensile strengths and the full curves of water absorption of the glass-fiber-reinforced concrete (GFRC) and polypropylene-fiber-reinforced concrete (PPFRC) were obtained. The strength differences and water absorption properties of GFRC/PPFRC were analyzed in depth. Scanning electron microscope observation was undertaken to analyze the mechanism of the water/binder ratio and fiber effects. The results showed that the water/binder ratio can affect the optimal fiber content. When discussing the effect of fibers on the improvement of concrete mechanical or microstructural properties, the influence of the water/binder ratio should be considered. The improvement effect of GF on water absorption was significantly superior to that of PPF. When the water/binder ratio was 0.30, the water absorption of GFRC and PPFRC tended to be stable as the test proceeded, while when the water/binder ratio increased to 0.35, the water absorption of the GFRC and PPFRC with the highest fiber dosage still increased with the prolongation of testing time.