Abstract This study aimed to obtain and characterize a polycrystalline diamond body (PCD) sintered with 15 wt% Nb binder, through the high-pressure high-temperature (HPHT) sintering techniques at three different temperatures of 1650 °C, 1750 °C, and 1850 °C, with a pressure of 7.7 GPa. Characterizations on the starting powders were performed before and after high energy ball milling, and then the obtained mixture was sintered. The results showed that niobium could perform as a good binder for the sintering PCD at the specified concentration, achieving relative densities in the range of 96% to 100% for all three sintering temperatures. Also, analyses of the electron micrographs and the Raman spectrograms showed that there was no graphitization, a common problem in this type of material, and there was uniform dispersion of the niobium at the interfaces of the diamond particles, and no cracking.