High-efficiency nanophotocatalysts with large specific surface areas have a broad range of application prospects in the catalytic oxidation treatment of organic pollutants in wastewater. A chemical method was used to synthesize a TiO2 nanophotocatalyst with a mesoporous structure upon which a rare earth metal (Nd) was deposited, namely Nd-TiO2-SBA-15 (NTS). The prepared NTS was characterized using X-ray diffractometry, transmission electron microscopy, Raman spectroscopy, and X-ray photoelectron spectrometry. The photocatalytic mechanism was explored using scavenger experiments with photoinduced carriers combined with total organic carbon and UV-Vis measurements. At the same time, the kinetic properties of the NTS photocatalytic degradation of methyl orange (MO) were evaluated. The results showed that the deposition of TiO2 nanoparticles on the surface of the SBA-15 molecular sieve did not change the mesoporous structure, and Nd was uniformly distributed on the surface of the nanophotocatalyst. The photogenerated holes of the NTS played an important role in the photocatalysis process. In addition, the synthesized NTS had good adaptability in the range of pH 2-10. At pH 4, the reaction rate constant (k) of the MO photocatalytic degradation by NTS was 0.011825 mg·(L·min)-1, and the adsorption equilibrium constant (K) was 0.051359 L mg-1. In addition, the photocatalytic degradation rate of MO by NTS remained above 70%, even when the NTS was recycled four times. The NTS showed a good performance after recycling. This work provides a good foundation for the large-scale application of NTS.