Abstract In this paper, environmental strength degradation of 180 different adhesive single lap joints (SLJ), including mono-adhesive Araldite 2015, mono-adhesive Araldite AV138, and a mixed-adhesive of Araldite 2015 and Araldite AV138 subjected to moist conditions are experimentally studied. Four different moist conditions, i.e. dry, 75.3, 84.2 RH% and immersion in tap water, have been taken into consideration and the specimens are tested after exposing to these environments at room temperature for 0, 35, 80 and 270 days. The specimens have been tested in two different strain rate, i.e. 1 mm/min and 100 mm/min. The results reveal that although, in a dry environment, mixed-adhesive joints have higher failure loads in comparison to mono-adhesive SLJs, in a moist environment, they have the highest reduction in static failure load with regard to the mono-adhesive ones. Moreover, despite the finally brittle trend in failure load, mixed-adhesives manifest a behavior very similar to ductile mono-adhesives regarding elongation. Analytical predictions of failure load are also consistent with the experimental observations in dry condition.