The granular cold water swelling oat starch was prepared by subcritical ethanol-water, and the changes of properties and structure on oat starch were investigated. The oat starch was modified at the temperature of 95 °C and ethanol concentration of 48% and showed a higher cold water swelling ability of 22.58 g/g, whereas native oat starch was 6.73 g/g. Modified oat starch granule was kept intact, and it was swollen when dispersing in the water. The gelatinization enthalpy declined to 0 J/g. The surface of modified oat starch granules was honeycomb and porous observed by scanning electron microscope. The X-ray diffraction showed the A-type crystal decreased and the V-type crystal increased, and the result was quantitatively confirmed by solid-state 13C NMR spectroscopy. The ratio of 1047 cm-1/1022 cm-1 (determined by Fourier transform infrared spectroscopy) of modified oat starch was decreased. The molecular weight distribution of modified oat starch was slightly reduced, and the amylose content increased from 26.18% to 31.68%, and only a small amount of carbohydrates leached during the modification. Subcritical ethanol-water modification improved the cold water swelling ability of oat starch. The starch crystals changed from A-type to V-type provide a potential mechanism of subcritical ethanol-water modified oat starch.