Three dimensional (3D) substrates based on natural and synthetic polymers enhance the osteogenic and mechanical properties of the bone tissue engineering scaffolds. Here, a novel bioactive composite scaffolds from polycaprolactone /kappa-carrageenan were developed for bone regeneration applications. 3D PCL scaffolds were fabricated by 3D printing method followed by coating with carboxymethyl kappa-carrageenan. This organic film was used to create calcium and strontium phosphate layers via a modified alternate soaking process in CaCl 2 /SrCl 2 and Na2HPO4 solutions in which calcium ions were replaced by strontium, with different amounts of strontium in the solutions. Various characterization techniques were executed to analyze the effects of strontium ion on the scaffold properties. The morphological results demonstrated the highly porous with interconnected pores and uniform pore sizes scaffolds. It was indicated that the highest crystallinity and compressive strength were obtained when 100% CaCl2 was replaced by SrCl2 in the solution (P-C-Sr). Incorporation of Sr onto the structure increased the degradation rate of the scaffolds. Mesenchymal stem cells (MSCs) culture on the scaffolds showed that Sr effectively improved attachment and viability of the MSCs and accelerated osteogenic differentiation as revealed by Alkaline phosphatase activity, calcium content and Real Time-Reverse transcription polymerase chain reaction assays.