LAUSR

Abstract A high activity ferrite Pr 0.3 Sr 0.7 Ti 0.3 Fe 0.7 O 3−δ (PSTF) has been synthesized and examined as a cathode of solid oxide electrolysis cell (SOEC) for direct high-temperature steam electrolysis. The SOEC with a configuration of PSTF|YSZ|LSM-YSZ was operated under H 2 O concentrations ranging from 20%H 2 O/Ar to 60%H 2 O/Ar and exhibited excellent electrochemical performances. Polarization resistance of the electrolyzer was as small as 0.43 Ω cm 2 in 60%H 2 O/Ar at 1.85 V at 800 °C. According to AC impendence spectra analyzing, gas diffusion process was the rate-determine-step (RDS) under smaller current density, while under larger current density, transport properties in the electrodes and the interfaces of electrode/electrolyte was RDS. The electrochemical properties of PSTF cathodes were systematically investigated and compared when they were exposed to gas atmosphere with and without safe gas (H 2 ). The obtained results demonstrated that PSTF electrode could conceivably avoid any hydrogen feeding for steam electrolysis.