Progressive wear based tool failure analysis during dry and MQL assisted sustainable micro-milling

Photo from wikipedia

Abstract Micro-milling tools suffer high wear rate and early edge-chipping owing to their small sizes. Mechanism of various wear modes of a coated tool with the progression of micro-milling along… Click to show full abstract

Abstract Micro-milling tools suffer high wear rate and early edge-chipping owing to their small sizes. Mechanism of various wear modes of a coated tool with the progression of micro-milling along with the conditions for their onset was not systematically explored in literature. To understand the edge-chipping scenario with the progression of wear, a comprehensive tribological analysis is presented in this article considering the cumulative effects of process mechanics, material deformation mechanism, tool geometry, lubrication, and process parameters during micro-milling of Ti-6Al-4V using 500 μm TiAlN-coated WC/6Co end-mills. The apparent friction coefficient at the chip-tool-workpiece interface remains very high, in the range of 0.97 – 0.84 in dry micro-milling that reduces to 0.60 – 0.50 under sustainable minimum quantity lubrication (MQL). When a fresh tool is engaged, it undergoes rapid wear for initial 15 mm length of cut. Thereafter, the tool undergoes gradual non-adhesive wear for another 40 – 70 mm cut. As the edge radius increases with machining time, the corresponding minimum uncut chip thickness (hmin) also increases proportionally. When hmin exceeds 12% (for MQL) or 34% (for dry) of the set feed per flute, strong adhesion occurs at the cutting edge, and the process is dominated by the non-cutting passes. Normal stresses within the ploughing-dominant region also remain reasonably high (10 – 18 GPa). Initially the coating, and thereafter the adhered layer, helps sustaining such high normal stresses. Once the adhered layer dislodges, the exposed substrate fails to sustain high stresses leading to edge-chipping. As compared to dry micro-milling, application of MQL helps decreasing abrasion rate, assisting in chip-evacuation, discouraging adhesion, and extending the tool-life; however, the same unfavourably increases the intensity of stresses within the ploughing-dominant region making the tool-tip more vulnerable to chipping.

Keywords: analysis; micro milling; edge; wear; mql; micro

Journal Title: International Journal of Mechanical Sciences
Year Published: 2021

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.