Abstract Novel Ce-rich phases Ce 4 RuAl and Ce 23 Ru 7+ x Al 4- x (0 ≤  x  ≤ 2.97) were found in the systematic investigation of the ternary Ce-Ru-Al system. Both compounds were investigated by scanning electron microscopy, EDX spectroscopy and X-ray diffraction methods. The Ce 4 RuAl compound crystallizes with a cubic structure of a Gd 4 RhIn type with lattice parameter a  = 13.7709(8) A (sp. gr. F -43 m , Z = 16). Its crystal structure was determined from single crystal X-ray data (R F  = 0.0241 for 741 independent reflections). The Ce 23 Ru 7+ x Al 4- x structure was established by X-ray powder diffraction. This compound belongs to Pr 23 Ir 7 Mg 4 structure type, space group P 6 3 mc . Cell parameters of Ce 23 Ru 7+ x Al 4- x at x  = 0.4 are: a  = 9.8137(4) A, c  = 22.2010(13) A. In both compounds Ce 4 RuAl and Ce 23 Ru 7+ x Al 4- x some of the Ce-Ru distances are short, equal to 2.630 A and 2.562 A, respectively. Crystal chemistry of these intermetallics is characterized by packing of non-linear layers in which the Ru-centered trigonal [Ce 6 ] prisms are connected via common vertices and edges, - similar to packing in the related Ce 7 Ru 3 and La 15 Rh 5 Cd 2 compounds.