LAUSR

Abstract A high strength (Yield strength ≥ 320 MPa) and high ductility (Tensile elongation ≥ 10%) die–cast aluminium alloy was first developed. The AlSiCuMgMn alloy processed by high pressure die casting can provide the high yield strength of 321 MPa, the high ultimate tensile strength of 425 MPa and the high ductility of 11.3%, after solution treated at 510 °C for 30 min and aged at 170 °C for 12 h. The alloy demonstrated 150% increase in ductility over the reported most advanced die–cast aluminium alloy, also comparable tensile properties to the 6000 series wrought aluminium alloys but with much lower manufacturing cost. The as–cast microstructure of the alloy mainly contained the primary α 1 –Al phase solidified in the shot sleeve, the secondary α 2 –Al phase solidified in the die, the Al–Si eutectic phase and the intermetallic phases Q–Al 5 Cu 2 Mg 8 Si 6 and θ–Al 2 Cu. The intermetallic phases Q and θ were dissolved into the α–Al matrix during solution. Nanoscale precipitates Q′ and θ′ were precipitated from the α–Al matrix for the strengthening of the alloy through ageing treatment. Multiple effects resulted in the high ductility of the alloy.