Abstract Rapid thermal annealing (RTA) has been performed on InGaAsP solar cells with the bandgap energy of 1 eV grown by molecular beam epitaxy. With the employment of RTA under an… Click to show full abstract
Abstract Rapid thermal annealing (RTA) has been performed on InGaAsP solar cells with the bandgap energy of 1 eV grown by molecular beam epitaxy. With the employment of RTA under an optimized condition, the open voltage was increased from 0.45 to 0.5 V and the photoelectric conversion efficiency was increased from 11.87–13.2%, respectively, which was attributed to the crystal quality improvement of p-type InGaAsP and therefore a reduced recombination current inside depletion region. The integral photoluminescence (PL) intensity of p-type InGaAsP increased to 166 times after annealing at 800 °C and its PL decay time increased by one order of magnitude. While the changes of nominally undoped and n-doped InGaAsP were negligible. The different behaviors of the effect of RTA on InGaAsP of different doping types were attributed to the highly mobile “activator” – beryllium (Be) atom in p-type InGaAsP.
               
Click one of the above tabs to view related content.