Abstract Oxidation resistance of textured Ti3AlC2 ceramics was measured in the temperature range 1273–1573 K. It was found that the oxidation was markedly anisotropic and the samples exhibited a better oxidation resistance when tested along a direction transverse to the c-axis. This behavior was attributed to the rapid diffusion of Al within its basal planes to form a passivating Al2O3 scale and it respected Ellingham diagrams. The scales formed had different compositions depending on the testing direction; this response was clearly resulting from the crystallographic orientation. Even at 1473 K after 20 h exposure, the samples tested in a direction transverse to the c-axis showed a reduced weight gain which was 45 times lower than one seen on a basal plane.